Thermal stability and flame retardancy of polyester, cotton, and relative blend textile fabrics subjected to sol-gel treatments
Articolo
Data di Pubblicazione:
2011
Citazione:
Thermal stability and flame retardancy of polyester, cotton, and relative blend textile fabrics subjected to sol-gel treatments / J. Alongi, M. Ciobanu, J. Tata, F. Carosio, G. Malucelli. - In: JOURNAL OF APPLIED POLYMER SCIENCE. - ISSN 0021-8995. - 119:4(2011 Feb 15), pp. 1961-1969. [10.1002/app.32954]
Abstract:
Polyester (PET), cotton (COT), and two relative blend textile fabrics were treated by sol-gel processes. Tetraethoxysilane (TEOS) was used as inorganic precursor of silica phases; furthermore, different TEOS/H2O ratios were examined to explore the effect of the presence of SiO2 on the thermal and fire stability of the textile fabrics investigated. The distribution and dispersion of SiO2 were observed by means of scanning electronic microscopy (SEM). SEM magnifications showed the formation of a continuous silica film located in the neighboring fibers; furthermore, in the case of PET, such a film incorporated silica particles with an average diameter ranging between 0.2 and 6 μm. The thermal and thermooxidative stabilities of the treated samples were investigated by thermogravimetric analysis: after the sol-gel treatment, the degradation mechanism was modified both in nitrogen and in air, and the improvement in the thermal stability was attributed to the presence of silica, which played a protective role in the degradation of the textile fabrics. Finally, we investigated the combustion behavior of the textile fabrics by cone calorimetry, measuring the time to ignition, the heat release rate, and the relative peak. The former was found to depend on the type of fabric; the latter generally evidenced a remarkable decrease for all of the treated samples, up to 35% compared to the neat counterparts. This indicated that the sol-gel treatments improved the flame retardancy of the PET/COT fabrics. This conclusion was also confirmed by limiting oxygen index tests, which evidenced burning kinetics changes in the presence of the silica coating.
Tipologia IRIS:
01 - Articolo su periodico
Keywords:
fibers; flame retardance; polyesters; silicas; thermogravimetric analysis (TGA); Materials Chemistry; Polymers and Plastics; Surfaces, Coatings and Films; Chemistry (all)
Elenco autori:
J. Alongi, M. Ciobanu, J. Tata, F. Carosio, G. Malucelli